Description:
Layer-Construction
● Spec.& Size: strengthening protection layer
Ageing-resistance layer
thickness:0.5-1.5mm waterproof layer
length:50-100m/rool strengthening adhesion layer
width:1.15-1.30m
It can be produced as requested
● Physical characteristics
|
item |
|
FS:(polythene compound membrane series) |
|
tension strength at break(N/cm) |
normal temperature ≥ |
60 |
|
60 ℃ ≥ |
30 |
|
pull lengthening at break % |
normal temperature ≥ |
400 |
|
-20 ℃ ≥ |
10 |
|
tear resistance N |
≥ |
20 |
|
water impermeability,30min no leaking |
|
0.3mpa |
|
cold bending ℃ |
< |
-20 |
|
beating elongation and shrinkage mm |
elongation < |
2 |
|
shrinkage < |
4 |
|
hotair ageing (80 ℃ X168h) |
holding of tension strength at break % ≥ |
80 |
|
holding of pull lengthening at break ≥ |
70 |
|
alkali-proof(10% Ca(OH)2)normal temperature X168h] |
holding of tension strength at break % ≥ |
80 |
|
holding of pull lengthening at break ≥ |
80 |
|
ozone ageing(40 ℃ X168h) 200pphm |
|
no craze |
|
phytotrons ageing |
holding of tension strength at break % ≥ |
80 |
|
holding of tension strength at break % ≥ |
70 |
Instruction:
● Polythene and Polypropylene Polymer Compound Waterproof Membrane is produced through new technology and processing method. It is one kind of Polythene Compound Waterproof Membrane products(FS2).
● It is of layer-construction. The surface layer is of strengthening protection, the middle layer is of ageing-resistance, and waterproofing material and beneath of strengthening adhesion. Every layer has special features which greatly improves the comprehensive function of the function of the product compared with the normal single-layer Waterproof materials.
Application Method:
● The application is easy and no pollution. It is mainly used in the middle of building for waterproofing. On this layer, other layers of protection and decoration are needed
● When application, pour the adhesive materials homogeneously on the smooth roof deck, then roll the membrane to make it fully adhered to the deck.
● The adhesive materials are usually made from water, 425#cement and 107# or other building glue at the volume rate of 3:6:1.
|